| Item | 840D/1 930dtex/1 |
1260D/1 1400dtex/1 |
1680D/1 1870dtex/1 |
840D/2 930dtex/dtex/2 |
1260D/2 1400dtex/dtex/2 |
1680D/2 1870dtex/dtex/2 |
1890D/2 2100dtex/dtex/2 |
1260D/3 1400dtex/dtex/3 |
|---|---|---|---|---|---|---|---|---|
| Breaking Strength | ≥ 69 | ≥ 103 | ≥ 132 | ≥ 137.2 | ≥ 215.6 | ≥ 279.3 | ≥ 305 | ≥ 305 |
| Breaking Strength Difference | ≤ 5.0 | ≤ 5.0 | ≤ 5.0 | ≤ 3.5 | ≤ 3.5 | ≤ 3.5 | ≤ 4.0 | ≤ 4.0 |
| Elongation | (At 22.6N) 7.5 ± 0.8 |
(At 33.0N) 7.5 ± 0.8 |
(At 44.0N) 8.0 ± 0.8 |
(At 44.1N) 8.0 ± 0.8 |
(At 66.6N) 8.0 ± 0.8 |
(At 88.2N) 8.0 ± 0.8 |
(At 100N) 9.5 ± 0.8 |
(At 100N) 9.5 ± 0.8 |
| Breaking Elongation | 22.0 ± 0.2 | 22.0 ± 0.2 | 22.0 ± 0.2 | 22.0 ± 0.2 | 22.0 ± 0.2 | 22.0 ± 0.2 | 23.0 ± 0.2 | 23.0 ± 0.2 |
| Breaking Elongation Difference | ≤ 6.0 | ≤ 5.5 | ≤ 5.5 | ≤ 5.5 | ≤ 5.5 | ≤ 5.5 | ≤ 6.0 | ≤ 6.0 |
| Adhesive Strength | ≥ 54 | ≥ 69 | ≥ 83 | ≥ 107.8 | ≥ 137.2 | ≥ 156.8 | ≥ 166.6 | ≥ 166.6 |
| Diameter/mm | 0.32 ± 0.3 | 0.43 ± 0.3 | 0.5 ± 0.3 | 0.55 ± 0.3 | 0.65 ± 0.3 | 0.75 ± 0.3 | 0.78 ± 0.4 | 0.78 ± 0.4 |
| Dip Pick Up | 4.2 ± 1.0 | 4.2 ± 1.0 | 4.2 ± 1.0 | 5.0 ± 1.0 | 5.0 ± 1.0 | 5.0 ± 1.0 | 5.0 ± 1.0 | 5.0 ± 1.0 |
| Hot Air Shrinkage 150℃ *30min | ≤ 4.5 | ≤ 4.5 | ≤ 4.5 | ≤ 8.0 | ≤ 8.0 | ≤ 7.0 | ≤ 7.0 | ≤ 7.0 |
| First Twist (Z) | 210 ± 15 | 190 ± 10 | 160 ± 10 | ... | ... | ... | ... | 320 ± 20 |
| Second Twist (S) | ... | ... | ... | 460 ± 15 | 370 ± 15 | 330 ± 15 | 320 ± 20 | 320 ± 20 |
| Moisture Regain | ≤ 1.0 | ≤ 1.0 | ≤ 1.0 | ≤ 0.8 | ≤ 0.8 | ≤ 0.8 | ≤ 0.8 | ≤ 0.8 |